MECHANICAL COMPOSITION

Find Details Below for chemical composition

Hastelloy C - 22


Product Form
 Tensile (ksi) .2% Yield (ksi)Elongation %Hardness (HRb)
Plate (.25”-1.75”)112536289
Sheet (.038”-.15”)122635493
Bar (.50”-5.50”)122556089

Hastelloy C - 276

Product Form Tensile (ksi) .2% Yield (ksi)Elongation %
Bar110.052.662
Plate107.450.367
Sheet115.554.660
Tube & Pipe105.445.470

Inconel 600

Product Form  ConditionTensile (ksi).2% Yield (ksi) Elongation (%) Hardness (HRB)
Rod & BarCold-Drawn80-10025-5035-5565-85
Rod & BarHot-Finished80-10030-5035-5565-85
Tube & PipeHot-Finished75-10025-5035*55-
Tube & PipeCold-Drawn80-10025-5035-5588 Max
PlateHot-Rolled80-10530-5035-5565-85
SheetCold-Drawn80-10030-4535-5588 Max

Inconel 625

Temp° F Tensile (psi) .2% Yield (psi) W
70144,00084,00044
400134,00066,00045
600132,00063,00042.5
800131,50061,00045
1000130,00060,50048
1200119,00060,00034
140078,00058,50059
160040,00039,000117

Incoloy 800H / HT

Product Tensile (ksi) .2% Yield (ksi) Elongation (%)
Rod & Bar 75-10030-60 60-30

Incoloy 825

Tensile (ksi) .2% Yield (ksi)
8530-35

Monel 400

Product Form ConditionTensile (ksi).2% Yield (ksi)Elongation (%)Hardness (HRB)
Rod & Bar Annealed 75-9025-5060-3560-80
Rod & BarCold-Drawn Stress Relieved 84-12055-10040-2285-20 HRC
PlateAnnealed 70-85 28-5050-3560-76
SheetAnnealed 70-85 30-4545-3565-80
Tube & Pipe SeamlessAnnealed 70-8525-4550-3575 max *

Monel K - 500

Product Form ConditionTensile (ksi).2% Yield (ksi)Elongation % Hardness
Rod & BarHot-Finished/Aged140-190100-15030-2027-38 HRC
Rod & Bar
Hot Finished/Annealed90-11040-6045-2575-90 HRB
Rod & Bar
Hot Finished/Annealed/Aged130-16585-12035-2024-35 HRC
Rod & Bar
Cold-Drawn/Aged135-18595-16030-1525-41 HRC
Rod & Bar
Cold-Drawn/Annealed/Aged130-19085-120
30-2024-35 HRC
PlateHot-Finished/Aged140-180100-13530-2027-37 HRC
SheetCold-Rolled/Annealed90-10540-6545-2585 HRB Max

Nickel 200 /201

Material Form and Condition Tensile (ksi) .2% Yield (ksi) Elongation (%)Hardness (HRB)
Rod & BarHot Finished60-8515-4555-3545-80
Rod & BarCold Drawn/Annealed or Hot-Finished/Annealed55-7515-3055-4045-70
plateHot-Rolled/Annealed 55-8015-4060-4045-75
sheetAnnealed 55-7515-3055-4070 max
Tube & PipeSeamless Annealed 55-7512-3060-4070 max

Titanium

Titanium Grade 2

Hardness, Knoop 170170
Hardness, Rockwell B8080
Hardness, Vickers145145
Tensile Strength, Ultimate344 MPa49900 psi
Tensile Strength, Yield275 - 410 MPa39900 - 59500 psi
Elongation at Break20%20%
Reduction of Area35%35%
Modulus of Elasticity105 GPa15200 ksiIn Tension
Compressive Modulus110 GPa16000 ksi
Poisson's Ratio0.37 0.37 
Izod Impact114 - 171 J84.1 - 126 ft-lb
Fatigue Strength300 MPa43500 psi1E+7 cycles, Unnotched
Fatigue Strength425 MPa61600 psi30,000 cycles, Unnotched
Fracture Toughness 66 MPa-m½60.1 ksi-in½K(Q); annealed
Shear Modulus45 GPa6530 ksi

Titanium Grade 5

Hardness, Brinell 379379
Hardness, Knoop414414
Hardness, Rockwell C4141
Hardness, Vickers396396
Tensile Strength, Ultimate1170 MPa170000 psi
Tensile Strength, Yield1100 MPa160000 psi
Elongation at Break10%10 %
Modulus of Elasticity114 GPa16500 ksi
Compressive Yield Strength1070 MPa155000 psi
Notched Tensile Strength1550 MPa225000 psi
Ultimate Bearing Strength2140 MPa310000 psi
Bearing Yield Strength1790 MPa260000 psi
Poisson's Ratio0.330.33
Charpy Impact23 J17 ft-lb
Fatigue Strength160 MPa23200 ksi
Fatigue Strength700 MPa102000 psi
Fracture Toughness43 MPa-m½39.1 ksi-in½
Shear Modulus44 GPa6330 ksi
Shear Strength760 MPa110000 psi

Titanium Grade 7

Hardness, Brinell 200200
Hardness, Knoop222222
Hardness, Rockwell B7575
Hardness, Rockwell C1111
Hardness, Vickers209209
Tensile Strength, Ultimate344 MPa49900 psi
Tensile Strength, Yield275 - 410 MPa39900 - 59500 psi
Elongation at Break20 %20%
Modulus of Elasticity105 GPa155000 psi
Compressive Modulus110 GPa16000 ksi
Poisson's Ratio0.370.37
Shear Modulus45 GPa6530 ksi